F-系列

迅速熔化，不浮于液面，加快成渣速度，提高脱磷、脱硫效果，对渣系的调整有良好的效果，降低吹炼综合成本；Rapid melting, does not float on the liquid surface, accelerates the slag formation speed, improves the dephosphorization, desulfurization effect, has a good effect on the adjustment of the slag system, reduces the comprehensive cost of blowing;

成分稳定、生产调节方便，有益于规模操作，减少操作随意性；Stable composition, convenient production adjustment, beneficial to scale operation, reduce operation randomness;

无喷溅，无返干，无烟尘，缩短冶炼周期，提高转炉作业率；No spatter, no backdrying, no smoke, shorten the smelting cycle, improve the operation rate of converter;

粒度均匀，压球强度高，无粉尘，不影响环境和作业；Uniform particle size, high pressure ball strength, no dust, does not affect the environment and operation;

完全可替代传统化渣助熔类产品，减少成本，同时在不减少废钢用量的情况下，从实际收得率可增加效益5~10元/吨钢。It can completely replace the traditional slag fusing products, reduce the cost, and at the same time, without reducing the amount of scrap steel, the actual yield can increase the benefit of 5~10 yuan/ton steel.

M-系列

冶炼前期化渣快，可缩短纯供氧时间30-60秒Smelting slag fast, can shorten the pure oxygen supply time 30-60 seconds

冶炼中期防“返干”，防喷溅、防粘枪，有利于安全生产Smelting in the middle of the anti-" back dry ", anti-splash, anti-stick gun, conducive to safe production

锰基无氟化渣剂球吨钢使用3-5kg情况下，终点钢水余锰可增加0.01-0.02%. The residual manganese in the final molten steel can be increased by 0.01-0.02% when the ball ton steel is 3-5kg

渣中带Fe降低，铁损减少，钢铁料消耗可降1.5-5kg/t，累计直接经济效益达2~5元/t钢. The Fe in the slag is reduced, the iron loss is reduced, the steel material consumption can be reduced by 1.5-5kg/t, and the cumulative direct economic benefit can reach 2 to 5 yuan /t steel